Two-Component RTV Rubbers (for moldmaking)

Two-component RTV silicone rubber compounds for moldmaking are suitable for mold masters for molding with polyester resin, epoxy resin, urethane foam, wax, plaster, and low-melt-point metal alloys. These RTV rubber compounds allow accurate reproduction of the shape of the original. They are easy to use and are thus used widely in industrial applications, as well as by hobbyists looking to create the perfect replica

Features

 

Workability

 

The base compound and curing agent are mixed and then poured into the mold to create a silicone rubber mold quickly. Workable time and cure time can be adjusted.

 

Mold-releasability

 

The cured rubber releases easily from the mold, so mold-release agents (soapy water, wax, etc.) are unnecessary.

 

Dimensional stability

 

These rubbers offer good dimensional stability, with little shrinkage.

 

Flowability

 

They have excellent flowability, so the original form is reproduced accurately. This includes even intricate shapes and details such as fingerprints and wood grain.

 

Non-exothermic

 

No heat is generated during curing, meaning no adverse effects to the original.
















 


Application

Grade

Curing method

Before curing Appearance

Features

General purpose

KE-12

Condensation

White

Good working properties.

KE-14

Condensation

Grayish white

Good working properties.

KE-17

Condensation

Grayish white

Good working properties.

For welder molding

KE-113

Condensation

Reddish brown

High hatrdness.

KE-24

Condensation

Grayish white

High hatrdness.

KE-26

Condensation

Grayish white

High hatrdness.

High-strength condensation-cure type

KE-1414

Condensation

Grayish white

Curing agent for skin-molding available.

KE-1415

Condensation

Grayish white

Hardness: 20°

KE-1416

Condensation

Grayish white

Hardness: 15°

KE-1417

Condensation

Grayish white

Improves urethane resistance. Hardness: 30°.

Grayish white

Improves urethane resistance. Hardness: 40°.

High-strength addition-cure type

KE-1300T

Addition

Translucent

 

KE-1310ST

Addition

Translucent

Improves urethane resistance.

KE1314-2

Addition

Translucent

Oil bleed.

KE-1316

Addition

Translucent

Low viscosity, low hardness.

KE-1600

Addition

Grayish white

High hardness.

KE-1603-A/B

Addition

Transparent

High transparency.

KE-1606

Addition

Transparent

High transparency.

Other

KE-1222-A/B

Addition

A:Blue
B:Deep flesh tone

Fast cure. Putty type.

KE-1241

Addition

Grayish white

For printing on curved surfaces.

     
     
 